| Analysis Item | Unit | Specification | Test Results | Test Method |
| Colored Granules | pcs/kg | ≤10 | 0 | SH/T 1541.1-2019 |
| Snakeskin Granules & tailing Granules | pcs/kg | ≤20 | 8 | SH/T 1541.1-2019 |
| Large And Small Granules | g/kg | ≤5 | 0.2 | SH/T 1541.1-2019 |
| Melt Mass-flow Rate (MFR) | g/10 min | 1.7–2.3 | 2.01 | GB/T 3682.1-2018 |
| Density (23°C) | g/cm³ | 0.917–0.923 | 0.9203 | GB/T 1033.2-2010 |
| Tensile Yield Strength | MPa | ≥8.0 | 9.12 | GB/T 1040.2-2022 |
| Tensile Strength At Break | MPa | ≥8.0 | 14.1 | GB/T 1040.2-2022 |
| Nominal Tensile Strain At Break | % | ≥400 | 469 | GB/T 1040.2-2022 |
| Haze (film thickness 0.030 mm) | % | Report | 11.8 | GB/T 2410-2008 |
| Fisheyes (0.8 mm) | pcs/1520 cm² | ≤6 | 3 | GB/T 11115-2009 |
| Fisheyes (0.4 mm) | pcs/1520 cm² | ≤15 | 11 | GB/T 11115-2009 |
| Impact Failure Mass (film thickness 0.030 mm) | g | Report | 137 | GB/T 9639.1-2008 |